ZG-P-7165/ZG-I-7249,Poly ISO For Shoe Sole,High Density Low Hardness Sole Pu
Poly ISO For Shoe Sole
High Density Low Hardness Sole Pu
Medium and low-hardness and medium and low-density PU Resin for sole of casual shoes for both men and women
Characteristic: Medium and low hardness, medium and &©|160;low density.
Application: Applicable to the production of medium soles of casual shoes for both men and women
Typical properties of PU Resin
Name of products Appearance Viscosity£¨Pa¡¤s/50℃£© Density£¨g/cm3/40℃£© Package£¨kg£©
ZG-P-7165 White or pale yellow, liquid, no foreign material 0.50-1.00 1.16-1.20 18
ZG-I-7249 Tran***rent liquid, no foreign material 0.10-0.30 1.18-1.20 20
Reference shipments ratio: A/B=30/23(barrel)
Catalysts and auxiliary agents:
ZG-P-7165/ZG-AC-2/water=18kg/220g/60-80g
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Poly Isocyanate Prepolymer Molding conditions & physical properties:
Reactivity Technical index Test item Reference physical properties
Reference ratioP+C/I 100/87-89 Molded density of sole£¨g/cm3£© 0.38~0.45
Using temperature£¨℃£© material: 45-50; B material:38-42 Hardness (type A) 40~55
Cream time£¨s£© 6~9 Tensile strength£¨***£© 3.5~4.5
Rise time£¨s£© 30~45 Elongation£¨£¥£© 350~450
Metal mold temperature£¨℃£© 55~65 NBS abrasion resistance£¨£¥£© ¡Ý10%
Demould time£¨min£© 4.0~6.0 Free foam density£¨g/cm3£© 0.15~0.18
Folding endurance (room temperature)(40,000 gap length mm) £¼8
Polyurethane Resin For Shoe Sole
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for refere |
| Company: |
Zhejiang HengTaiYuan P.U Co., Ltd.
|
| Contact: |
Ms. nina ye |
| Address: |
Science Park No.1 Road,Industrial Zone,Wenling City,Zhejiang Province,China |
| Postcode: |
317500 |
| Tel: |
0576-86992777 |
| Fax: |
0576-86992777 |
| E-mail: |
|
|
|
|
Home